UNS N08020鎳基合金
產品名稱：ALLOY20/UNS N08020
國際通稱：Alloy 20合金、UNS N08020、NS143、Inconel alloy20/NAS 335X、W.Nr.2.4460
Nicrofer 3620 Nb-alloy20、ATI 20
各國標準：ASTM B463/ ASME SB463、ASTM A240/ ASME SA240、ASTM B729/ ASME SB729
主要成分：
| Element | Wt, % |
|---|---|
| Carbon [C] | ≤0.07 |
| Manganese [Mn] | ≤2.00 |
| Phosphorus [P] | ≤0.045 |
| Sulfur [S] | ≤0.035 |
| Silicon [Si] | ≤1.00 |
| Nickel [Ni] | 32.00~38.00 |
| Chromium [Cr] | 19.00~21.00 |
| Molybdenum [Mo] | 2.00~3.00 |
| Copper [Cu] | 3.00~4.00 |
| Niobium+Tantalum [Nb+Ta] | 8xCarbon~1 |
| Iron | Remainder |
*The tabulated values are abstracted from ASTM B462 Gr. UNS N08020.
物理性能：
| Alloy | Tensile Strength, min. | Yield Strength, min. | Elongation, min. | Reduction of Area, min. | ||
|---|---|---|---|---|---|---|
| ASTM B462 | ksi | MPa | ksi | MPa | % | % |
| UNS N08020 | 80 | 551 | 35 | 241 | 30.0 | 50.0 |
*All values shall be measured at room temperature.
*Alloy 20 flanges shall be supplied in stabilized-annealed condition.
熱處理：900-1150℃之間保溫1-2小時，快速空冷或水冷。
機械性能：抗拉強度：σb≥550Mpa，屈服強度σb≥240Mpa：延伸率：δ≥30%，硬度；HB135-220
耐腐蝕性及主要使用環境：
Alloy 20合金具有很多優異性能的耐蝕合金，對氧化性和中等還原性腐蝕 有很好的抵抗能力，具有優異的抗應力腐蝕開裂能力和好的耐局部腐蝕能力在很多化工工藝介質中有滿意的耐蝕特性。
有優異的抗應腐蝕開裂能力和好的耐局部還原性復合介質腐蝕，運用于硫酸環境及含有鹵族離子及金屬離子的硫酸溶液工業裝置。
配套焊接材料及焊接工藝：Alloy 20合金的焊接建議采用AWS A5.14焊絲ERNiCrMo-3或AWS A5.11焊條ENiCrMo-3，焊接工藝及指導書歡迎來電索取。
應用領域有：硫酸酸洗設備、磷酸生產設備、石油化工裝備、煤化工、海洋平臺、海水淡化、復合板、波紋管膨脹節等行業和產品。